Regular Butyl & Halogenated Butyl Rubber

Butyl rubber (IIR) is a synthetic rubber, a copolymer of isobutylene with isoprene. Providing excellent air retention, it is widely used for tire inner liners among other applications.

X_Butyl® RB 301 Regular Butyl Rubber
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 51 MU ISO 289 / ASTM D 1646 ML (1+8) 125 °C
Unsaturation 1,85 %(Mol) (*)
Antioxidant non-staining ≥ 0,03 wt % (*)
Ash Content ≤ 0,3 wt % ISO 247 / ASTM D 5667
Volatile Content ≤ 0,3 wt % ISO 248 / ASTM D 5668
X_Butyl® RB 402 Regular Butyl Rubber
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 33 MU ISO 289 / ASTM D 1646 ML (1+8) 125 °C
Unsaturation 2,25 %(Mol) (*)
Antioxidant non-staining ≥ 0,03 wt % (*)
Ash Content ≤ 0,3 wt % ISO 247 / ASTM D 5667
Volatile Content ≤ 0,3 wt % ISO 248 / ASTM D 5668

Chloroprene Rubber

Chloroprene rubber (international ASTM/DIN-abbreviation: CR) is a high-performance material with a wide variety of applications. Baypren® is the brand-name of the ARLANXEO range of polymers based on 2-chloro-1,3-butadiene (chloroprene), which are manufactured by water-based emulsion polymerization....

Baypren® 116 M 45 XD-modified Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 45 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Density 1,23 g/cm3 Internal Method
Baypren® 210 M 43 M-modified Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 43 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Density 1,23 g/cm3 Internal Method
Baypren® 210 M 48 M-modified Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 48 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Density 1,23 g/cm3 Internal Method
Baypren® 211 M 39 M-modified Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 39 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Density 1,23 g/cm3 Internal Method
Baypren® 214 M 55 Precrosslinked Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 55 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Density 1,23 g/cm3 Internal Method
Baypren® 215 M 50 Precrosslinked Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 50 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Density 1,23 g/cm3 Internal Method
Baypren® 216 M 43 XD-modified Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 43 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Density 1,23 g/cm3 Internal Method
Baypren® 216 M 49 XD-modified Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 49 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Density 1,23 g/cm3 Internal Method

Ethylene Propylene Diene Rubber

EPDM is typically used in outdoor applications and at elevated temperatures of up to 150 °C. It's used in both automotive and industrial applications such as automotive sealing systems, coolant hoses, windshield wipers, oil additives, roof sheeting, window gaskets, conveyor belts, as well as wire...

Keltan® 0500R Downsheared
Property Nominal Value Test Method Condition Temperature
Melt Flow Index 190 °C 11 g/10mi ASTM D 1238
Molecular Weight Distribution Narrow Internal Method
Ethylene Content 49 wt % ASTM D 3900
Density 0,86 g/cm3 Internal Method
Keltan® 2470C Low Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 22 MU ISO 289 / ASTM D 1646 ML (1+4) 125 °C
Molecular Weight Distribution CLCB Internal Method
Ethylene Content 70,5 wt % ASTM D 3900
ENB Content 4,5 wt % ASTM D 6047
Density 0,86 g/cm3
Keltan® 2470E Low Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 22 MU ISO 289 / ASTM D 1646 ML (1+4) 125 °C
Molecular Weight Distribution CLCB Internal Method
Ethylene Content 69 wt % ASTM D 3900
ENB Content 4,2 wt % ASTM D 6047
Density 0,86 g/cm3 Internal Method
Keltan® 2470S Low Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 25 MU ISO 289 / ASTM D 1646 ML (1+4) 125 °C
Molecular Weight Distribution CLCB Internal Method
Ethylene Content 69 wt % ASTM D 3900
ENB Content 4,2 wt % ASTM D 6047
Density 0,86 g/cm3 Internal Method
Keltan® 3470 Low Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 36 MU ISO 289 / ASTM D 1646 ML (1+4) 125 °C
Molecular Weight Distribution CLCB Internal Method
Ethylene Content 68 wt % ASTM D 3900
ENB Content 4,6 wt % ASTM D 6047
Density 0,86 g/cm3 Internal Method
Keltan® 5170 Medium Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 59 MU ISO 289 / ASTM D 1646 ML (1+4) 125 °C
Molecular Weight Distribution Narrow Internal Method
Ethylene Content 71 wt % ASTM D 3900
ENB Content 1,5 wt % ASTM D 6047
Density 0,86 g/cm3 Internal Method
Keltan® 5470
Regional
Medium Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 55 MU ISO 289 / ASTM D 1646 ML (1+4) 125 °C
Molecular Weight Distribution CLCB Internal Method
Ethylene Content 70 wt % ASTM D 3900
ENB Content 4,6 wt % ASTM D 6047
Density 0,86 g/cm3 Internal Method
Keltan® 5470C Medium Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 55 MU ISO 289 / ASTM D 1646 ML (1+4) 125 °C
Molecular Weight Distribution CLCB Internal Method
Ethylene Content 66 wt % ASTM D 3900
ENB Content 4,6 wt % ASTM D 6047
Density 0,86 g/cm3 Internal Method
Keltan® 6470C High Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 63 MU ISO 289 / ASTM D 1646 ML (1+4) 125 °C
Molecular Weight Distribution CLCB Internal Method
Ethylene Content 64 wt % ASTM D 3900
ENB Content 4,8 wt % ASTM D 6047
Density 0,86 g/cm3 Internal Method
Keltan® 8570C High Mooney
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 80 MU ISO 289 / ASTM D 1646 ML (1+4) 125 °C
Molecular Weight Distribution CLCB Internal Method
Ethylene Content 66 wt % ASTM D 3900
ENB Content 5,0 wt % ASTM D 6047
Density 0,86 g/cm3 Internal Method

Ethylene Vinyl Acetate Rubber

ARLANXEO’s EVM rubbers are sold under the tradenames Baymod® L, Levamelt® and Levapren®. EVM rubbers are produced by copolymerization of ethylene and vinyl acetate. Our ethylene-vinyl acetate copolymers are used as synthetic rubbers, or as modifiers in thermoplastics, specifically PVC. The main...

Levamelt® 700 General Purpose Grades
Property Nominal Value Test Method Condition Temperature
Melt Flow Index 190 °C 4 g/10mi ISO 1133
Vinyl Acetate Content 70 wt % Internal Method LP 015
Density 1,07 g/cm3 Internal Method
Levapren® 400 General Purpose Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 20 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Vinyl Acetate Content 40 wt % Internal Method LP 015
Density 0,98 g/cm3 Internal Method
Levapren® 450 General Purpose Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 20 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Vinyl Acetate Content 45 wt % Internal Method LP 015
Density 0,99 g/cm3 Internal Method
Levapren® 500 General Purpose Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 27 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Vinyl Acetate Content 50 wt % Internal Method LP 015
Density 1,00 g/cm3 Internal Method
Levapren® 500 XL Special Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 55 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Vinyl Acetate Content 50 wt % Internal Method LP 015
Density 1,00 g/cm3 Internal Method
Levapren® 600 General Purpose Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 27 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Vinyl Acetate Content 60 wt % Internal Method LP 015
Density 1,04 g/cm3 Internal Method
Levapren® 600 XL Special Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 55 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Vinyl Acetate Content 60 wt % Internal Method LP 015
Density 1,04 g/cm3 Internal Method
Levapren® 700 General Purpose Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 27 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Vinyl Acetate Content 70 wt % Internal Method LP 015
Density 1,07 g/cm3 Internal Method
Levapren® 800 General Purpose Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 28 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Vinyl Acetate Content 80 wt % Internal Method LP 015
Density 1,11 g/cm3 Internal Method

Hydrogenated Nitrile Butadiene Rubber

ARLANXEO's HNBR products, summarized under the Therban® brand, offer excellent properties wherever high temperature and fluid resistance is needed. The polarity of HNBR is directly influenced by the ACN content. Higher ACN increases the polymer's polarity and, therefore, resistance in non-polar...

Therban® 3406 Fully Saturated (suitable for peroxide crosslinking) Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 63 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Acrylonitrile Content 34 wt % ISO 24698-1
Residual Double Bonds 0,9 % IR Spectroscopy
Density 0,95 g/cm3 Internal Method
Therban® 3407 Fully Saturated (suitable for peroxide crosslinking) Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 70 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Acrylonitrile Content 34,0 wt % ISO 24698-1
Residual Double Bonds 0,9 % IR Spectroscopy
Density 0,95 g/cm3 Internal Method
Therban® 3907 Fully Saturated (suitable for peroxide crosslinking) Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 70 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Acrylonitrile Content 39,0 wt % ISO 24698-1
Residual Double Bonds 0,9 % IR Spectroscopy
Density 0,96 g/cm3 Internal Method
Therban® 4307 Fully Saturated (suitable for peroxide crosslinking) Grades
Property Nominal Value Test Method Condition Temperature
Mooney Viscosity 63 MU ISO 289 / ASTM D 1646 ML (1+4) 100 °C
Acrylonitrile Content 42,5 wt % ISO 24698-1
Residual Double Bonds 0,9 % IR Spectroscopy
Density 0,98 g/cm3 Internal Method